| TCL-MF ultra-low formaldehyde no-ironing resin Detailed information | Finishing Agent sort | |
| Product name: | TCL-MF ultra-low formaldehyde no-ironing resin | No Photo |
| Ingredients: | special modified dimethylol dihydroxy ethylene urea | |
| Physicochemical properties: | appearance: weakly yellow light transparent liquid pH value: 6-7 Free formaldehyde: ≤0.5% Solubility: mixed with any ratio of water |
|
| Characteristics and usage: | DP finish for cotton, linen, viscose, Tencel and its blended fabrics with chemical fibers. The fabric after treatment features good recovery, anti shrinking, and durability to washing, low strength loss, especially released formaldehyde ultra lower than 75ppm. | |
| Application methods: | dilute the resin and catalyst with water before application respectively, adding softener at last, stirring thoroughly, adjust working liquor to pH value 5-5.5 with HAc, for garment finish by immersion method, for fabric finish by padding method. Padding method: TCL-MF resin: 60-100 g/L CZ-3 catalyst: 20-25% ratio to resin Softener: moderate dosage Twice dipping twice padding (pick up 70%)---85¡æ stenter drying ---curing at 155¡æ for 3 minutes Immersion method: TCL-MF resin: 50-100 g/L CZ-3 catalyst: 20-25% ratio to resin Softener: moderate dosage Immersion (15-20 minutes)---water extraction (pick-up 70-80%)----drying (moisture regain 7-10%)----ironing---155¡æ curing for 4-7 minutes Practical dosage depends on trials, the treated fabric should have clean surface and acidic pH value. |
|
| Package and storage: | 25kg plastic drum, stored at room temperature, validity for 6 months | |
| Limited guarantee: | ||
| remark: | ||
TCL-MF ultra-low formaldehyde no-ironing resin